Colloid probe AFM study of thermal collapse and protein interactions of poly(N-isopropylacrylamide) coatings

Martin Cole, Nicolas Voelcker, Helmut Thissen, Roger Horn, Hans Griesser

    Research output: Contribution to journalArticlepeer-review

    27 Citations (Scopus)

    Abstract

    Graft coatings of poly(N-isopropylacrylamide) (pNIPAM) are of considerable interest for the reversible control of bio-interfacial interactions. In this study, graft coatings were prepared by free radical polymerisation from surface-bound polymerisable groups, on silicon wafers and quartz crystal microbalance (QCM) sensors. QCM with dissipation monitoring showed a gradual, extended phase change as the temperature increased. Colloid probe atomic force microscopy (CP-AFM) revealed a marked change in the compressibility of the coating below and above the lower critical solution temperature (LCST). Force curves showed an approximate 9-fold reduction in thickness between 24 °C and 38 °C, yet the collapsed coating at 38 °C still had a thickness significantly higher than the ellipsometrically determined dry thickness, indicating a residual extent of hydration above the LCST. At all temperatures, interaction force curves showed steric repulsion, though over different distances. There was little hysteresis between approach and retract force curves, which is evidence for almost instantaneous relaxation of the coating upon decompression. CP-AFM using a probe coated with bovine serum albumin (BSA) showed repulsive interactions with little approach/retraction hysteresis below the LCST, indicating lack of adhesion between the pNIPAM coating and the BSA-coated probe. In contrast, above the LCST the force curves on retraction were characteristic of adhesion, while the approach curves were still repulsive, and the adhesion increased in strength as the temperature was increased further beyond the LCST. Thus, QCM-D and CP-AFM data correlated well in showing a gradual nature of the phase transition and a concomitant gradual change in the interaction force with BSA.

    Original languageEnglish
    Pages (from-to)2657-2667
    Number of pages11
    JournalSoft Matter
    Volume6
    Issue number12
    DOIs
    Publication statusPublished - 2010

    Fingerprint Dive into the research topics of 'Colloid probe AFM study of thermal collapse and protein interactions of poly(N-isopropylacrylamide) coatings'. Together they form a unique fingerprint.

    Cite this