In situ polymerized hyperbranched polymer reinforced poly (acrylic acid) hydrogels

Nazila Dehbari, Javad Tavakoli, Simranjeet Khatrao, Youhong Tang

    Research output: Contribution to journalArticle

    11 Citations (Scopus)

    Abstract

    Hydrogels have been extensively investigated for use in various applications. Poly acrylic acid (PAA) is a common example, which has been widely used due to its super hydrophilicity properties, biocompatibility and biodegradability characteristics. However its poor mechanical properties, which have been addressed in many research studies, are known as a drawback that limits its applications. So, enhancing PAA mechanical properties using a hyperbranched polymer (HB) is the key question to be addressed in this research. Investigations of the mechanical properties of the PAA-HB hydrogel revealed 130% improvement in the ultimate tensile strength, indicating a two times enhancement compared to that of PAA. Statistical analysis showed that the overall effect of introducing notches (with different depths) on the selected mechanical properties of both PAA and PAA-HB was significant. Mechanical characterization of PAA-HB networks showed that significant improvement in the mechanical properties was achieved as the capability of water uptake increased by 20%. Characterization of the physical properties confirmed that participation of HB may form a PAA based hybrid material with good swelling properties. Those findings are attributed to the supramolecular structure of the HB, which can introduce physical entanglement between the PAA network structure and increase the crystallinity of the final hydrogel as compared to those from the PAA hydrogel.

    Original languageEnglish
    Pages (from-to)1995-2004
    Number of pages10
    JournalMaterials Chemistry Frontiers
    Volume10
    Issue number10
    DOIs
    Publication statusPublished - 2017

    Fingerprint Dive into the research topics of 'In situ polymerized hyperbranched polymer reinforced poly (acrylic acid) hydrogels'. Together they form a unique fingerprint.

    Cite this